THERMOCOAT-ROOF (TCC-510)
INSULATION MATERIAL FOR TERRACE ROOFS
AS INTERMEDIATE LAYER UNDER THE LINING
(HEAT-WATER-SOUND-FIRE)
|
| PACKING |
: 20 kg. Kraft bag |
| ASPECT |
: White Grained Dust |
| APPLICATION TEMP. |
: Between +5 / +30 o C
|
| CONSUMPTION |
: 7,5 - 8 kg. / m2 / cm. |
| THICKNESS OF APPLICATION |
: 1,5 - 2,0 cm. |
| DURATION OF APPLICATION |
: 4 hours (23 o C) |
| TOOLS FOR APPLICATION |
: Trowel , Plaster Pump |
| DRYING TIME |
: (23 o C - %50 at relative humidity )
First Layer Drying...................9 hours
Last Layer Drying................48 hours
Test Drying...........................28 days |
| APPLICATION SURFACE |
: Sloping Screed, Sloping Concrete
(Please refer to our tech.dep.for other substrates) |
| SHELF LIFE |
: 18 months in dry conditions |
|
| |
|
| THERMAL CONDUCTIVITY (T1) |
: 0,083 kcal/mh o C |
| COMPRESSIVE STRENGHT (CSII) |
: 3,16 N / mm2 (1,5-50N / mm2 ) |
| ADHESION STRENGHT |
: 6,4 Kgf / cm2 (≥ 3 Kgf / cm2 )** |
| TENSILE STRENGHT |
: 12,4 kgf/cm2 (≥6kgf/cm2)* |
| CAPILLARY WATER ABSORPTION (W1) |
: 0,121 kgm2sn0.5 |
| WATER REPELLENT (SURFACE) |
: 1,40mm (≤ 5mm)** |
| TOTAL HUMIDITY MOVEMENT |
1,062 mm/m (≤ 2mm/m)** |
| VAPOUR CONDUCTIVITY (µ) |
3 (≤ 15)** |
| SODIUM CHLORINE RESISTANCE |
5 % (≤ %10) ** |
| SODIUM SULPHATE RESISTANCE |
6 % (≤ %10) ** |
| SULFURIC ACID RESISTANCE |
5,9 % (≤ %10) ** |
| SOUND INSULATION VALUE |
18 db (1,5 cm / 500 Hz) |
| FIRE CLASS |
A-1 Non Flammable |
| |
| ** Standart value for ready mixed insulation plasters |
|
|
DESCRIPTION
Single layer, multi-purpose terrace roof insulation material in mortar form. It is an intermediate layer under finishing lining. The open cell porous natural aggregates, in it's mixture, provides
HEAT - SOUND - FIRE
insulation and it stops perspiration on the surface by it's diffusion ability. It makes WATER insulation at the same time because of it's (positive direction) water repellent structure
APPLICATION AREAS
On the terrace roofs of buildings, on sloped roofs, on basement floors.
ADVANTAGES
Making heat, water, sound and fire insulation with one product.
Addition to the budget of heating and cooling costs.
No formation of heat and sound bridges because of it's jointless
structure. Because protective screed is not required, the load
effecting the building is decreased.
High fire resistance.
Stopping condensation (perspiration-mould-humidity).
Light, therefore no loading to the building.
Increasing the value of the building.
No cancerogen ingredients.
STORAGE - HANDLING
The bags should not be torn, pierced and opened before
usage and must be stowed maximum 10 rows in pallets.
Protect from frost and direct sun light.
HEALTH - SAFETY
TCC - 510 is produced from natural materials and
not hazardous to health
Does not contain cancerogen materials
> Dust mask should be used during mixing because of pollination.
|
|